Generation of carbon nanostructures with diverse morphologies by the catalytic aerosol-assisted vapor-phase synthesis method - 20/11/15
, Paulina Baran a, Przemysław Grzywacz a, Paweł Baran a, Jerzy F. Janik a, Agnieszka Różycka b, Maciej Sitarz b, Piotr Jeleń bBienvenue sur EM-consulte, la référence des professionnels de santé.
L’accès au texte intégral de cet article nécessite un abonnement.
| pages | 7 |
| Iconographies | 7 |
| Vidéos | 0 |
| Autres | 0 |
Abstract |
The Fe catalyst-supported aerosol-assisted synthesis method was used to prepare carbon products of diverse morphologies from toluene. Aerosol mist generation was accomplished with an ultrasonic device. An open-ended quartz boat for powder collection was placed in the maximum temperature zone of the tube reactor (850°C or 1000°C). The morphology of the products was studied by SEM and TEM microscopy. Structural characterization was provided by powder XRD, whereas Raman spectroscopy was used to determine the structural quality/homogeneity of the products. The hydrogen gas sorption capacity of the product prepared at 850°C was relatively high despite its rather moderate BET specific surface area.
Le texte complet de cet article est disponible en PDF.Keywords : Metallocenes, Carbon nanostructures, Nanotubes, Heterogeneous catalysis
Plan
Vol 18 - N° 11
P. 1198-1204 - novembre 2015 Retour au numéro
Article précédent
- Foreword
- Christophe Dujardin, Patrick Da Costa
- Ni–Al hydrotalcite-like material as the catalyst precursors for the dry reforming of methane at low temperature
- Rados?aw D?bek, Katarzyna Zubek, Monika Motak, Maria Elena Galvez, Patrick Da Costa, Teresa Grzybek
Bienvenue sur EM-consulte, la référence des professionnels de santé.
L’accès au texte intégral de cet article nécessite un abonnement.
Bienvenue sur EM-consulte, la référence des professionnels de santé.
L’achat d’article à l’unité est indisponible à l’heure actuelle.
Déjà abonné à cette revue ?