Bilayer zeolite films ZSM-5/ZSM-5, ZSM-5/EMC-1 and NaY/ZSM-5 were synthesized on α-alumina plates. The bottom ZSM-5 or faujasite Y (NaY) zeolite layers were obtained by direct hydrothermal synthesis or by using a seeding step followed by a secondary growth method, respectively, while the secondary growth method was used for the synthesis of all the top zeolite layers. A complete characterization of the obtained materials is proposed using various techniques, such as X-ray diffraction, scanning electron microscopy, X-ray fluorescence and nitrogen sorption measurements. Continuous and highly crystallized bi-layer zeolite films with thicknesses around 11–18 μm were obtained.

Des films composés de deux couches zéolithiques ZSM-5/ZSM-5, ZSM-5/EMC-1 et NaY/ZSM-5 ont été synthétisés sur des plaques en α-alumine. Les couches inférieures de zéolithes ZSM-5 ou de faujasite Y (NaY) ont été obtenues respectivement par synthèse hydrothermale directe ou par la méthode d’ensemencement suivie d’une étape de croissance secondaire, tandis que la méthode de croissance secondaire a été privilégiée pour la synthèse de toutes les couches supérieures de zéolithes. Une caractérisation complète des matériaux obtenus est proposée en utilisant diverses techniques, telles que la diffraction de rayons X, la microscopie électronique à balayage, la fluorescence des rayons X et des mesures de manométrie de sorption d'azote. Des films composés de deux couches zéolithiques hautement cristallisés avec une épaisseur variant entre 11 et 18 μm ont été obtenus.