We analyzed a single-piece plate-type hydrophilic acrylic posterior chamber intraocular lens (IOL) that was explanted due to a progressive loss of vision, which occurred 6years after uncomplicated phacoemulsification. Gross and light microscopy, as well as anterior segment optical coherence tomography (OCT) revealed granular deposits below the IOL surface. Light scattering, as measured with Scheimpflug photography and densitometry analyses was found to be increased; spectrophotometry demonstrated a decrease in the light transmittance of the explanted lens. The granular deposits within the IOL material were found to be composed of calcium by histochemical methods (alizarin red and Von Kossa stains). To our knowledge this is the only report of calcification of this IOL design.

Nous avons analysé un implant intraoculaire acrylique hydrophile, monobloc à trois haptiques, qui a dû être explanté à cause d’une diminution progressive de la vision, six années après phacoémulsification. Des analyses macroscopique et microscopique, ainsi qu’une tomographie à cohérence optique du segment antérieur ont révélé des dépôts granulaires sous la surface de l’implant. Les photographies Scheimpflug avec densitométrie ont mis en évidence une augmentation de la dispersion lumineuse ; la spectrophotométrie a montré une diminution de la transmission lumineuse de l’implant. Les analyses histochimiques par le rouge d’alizarine et la méthode de Von Kossa ont démontré que les dépôts granulaires dans le matériau de l’implant étaient composés de calcium. À notre connaissance, il s’agit du premier cas de calcification de cet implant.