Culture cellulaire d'ostéoblastes et de fibroblastes sur substituts osseux poreux en phosphate de calcium - 18/04/08

Doi : RCO-01-2003-89-1-0035-1040-101019-ART5 

J. Chouteau [1 et 2],

A. Bignon [3],

P. Chavassieux [4],

J. Chevalier [3],

M. Melin [5],

G. Fantozzi [3],

G. Boivin [4],

D. Hartmann [5],

J.-P. Carret [1 et 2]

Ver las filiaciones

Bienvenido a EM-consulte, la referencia de los profesionales de la salud.
Artículo gratuito.

Conéctese para beneficiarse!

Les céramiques en phosphate de calcium sont des substituts osseux synthétiques capables de combler des pertes de substance osseuse en servant de support à la repousse osseuse. Ce travail a consisté à étudier in vitro la culture d'ostéoblastes et de fibroblastes sur trois matériaux synthétiques de phosphate de calcium composés de 70 % d'hydroxyapatite et de 30 % de phosphate tricalcique-bêta. Ils se différenciaient par la taille de leurs macropores et par la présence ou non de microporosités sur leurs parois. Les caractéristiques mécaniques et physico-chimiques de chaque composé ont été analysées. Les cultures cellulaires ont été réalisées sur des disques de 10 mm de diamètre et 2 mm d'épaisseur. La viabilité cellulaire a été évaluée par test MTT à chaque temps d'observation. Une étude histologique appréciant l'invasion en profondeur des disques a été menée et la microscopie électronique à balayage a permis d'apprécier le comportement cellulaire au contact et à la surface du substitut. Il n'a pas été observé de cytotoxicité des trois composés. La croissance cellulaire s'est déroulée sur chaque substitut et pour chaque type cellulaire de manière exponentielle. Les cellules se sont développées en surface des composés en pontant les macropores et ont colonisé la profondeur des disques. Les macropores de plus de 300 µm ont semblé favoriser cette invasion. Une taille d'interconnexion de 15 µm est apparue suffisante pour permettre le passage cellulaire entre les macropores. La présence ou non de microporosités sur les parois n'a pas engendré de différence significative sur la prolifération cellulaire. Actuellement, les substituts osseux sont ostéoconducteurs mais non ostéo-inducteurs. L'association d'une culture de cellules ostéoblastiques sur un composé macroporeux de phosphate de calcium synthétique pourrait permettre la réalisation d'un substitut osseux ayant des propriétés ostéoinductrices.

Cellular culture of osteoblasts and fibroblasts on macroporous calcium-phosphate bone substitutes

Purpose of the study

Calcium phosphate ceramics are synthetic bone substitutes able to fill in bone destruction as a support of the bone growth. This work consisted in an in vitro assessment of osteoblasts and fibroblasts cultures on macroporous calcium-phosphate bone substitutes to analyze the interaction between cells and bone substitute.

Materials and methods

The macroporous ceramic was composed of 70 % hydroxyapatite and 30 % tri-calcium phosphate with known mechanical and physico-chemical properties. Three compounds were processed with different size of macropore and with or without microporosity on their surface. Cells were seeded on discs measuring 10 mm in diameter and 2 mm in thickness. Cellular viability was evaluated by the MTT test for every stage of observation. An histological study to observe the invasion in the depth of discs was performed. Scanning electron microscopy was used to analyze the cellular comportment in contact with the surface of substitutes.

Results

An exponential cellular growth was effective on each substitute with the two cellular types. Cells spread on the surface of the compounds covering macropores and colonized the depth of the discs. A size of macropore of 300 µm or more seemed to support this invasion. 15 µm sized interconnections appeared to be effective to allow cell migration between macropores. The cell proliferation was similar on substitutes with or without microporosity.

Conclusion

Biomaterials currently used as bone substitute are more or less osteoconductive but they have no osteoinductive property. A hybrid association of calcium-phosphate ceramic with osteogenic cells should promote the development of a calcium phosphate compound with osteoinductive capacity.


Mots clés : Substitut osseux , phosphate de calcium , hydroxyapatite , porosité , culture cellulaire

Keywords: Bone substitute , calcium-phosphate , hydroxyapatite , porosity , cell culture


Esquema



© 2003 Elsevier Masson SAS. Tous droits réservés.
Añadir a mi biblioteca Eliminar de mi biblioteca Imprimir
Exportación

    Exportación citas

  • Fichero

  • Contenido

Vol 89 - N° 1

P. 44-52 - janvier 2003 Regresar al número
Artículo precedente Artículo precedente
  • Réparation méniscale par fixations biodégradables : étude biomécanique comparative
  • R. Seil, S. Rupp, C. Jurecka, T. Georg, D. Kohn
| Artículo siguiente Artículo siguiente
  • Apport de la scie de Gigli pour l'ablation d'une tige fémorale sans ciment non descellée à effet de surface réhabitée
  • E. De Thomasson, O. Guingand, C. Mazel

Bienvenido a EM-consulte, la referencia de los profesionales de la salud.

Mi cuenta


Declaración CNIL

EM-CONSULTE.COM se declara a la CNIL, la declaración N º 1286925.

En virtud de la Ley N º 78-17 del 6 de enero de 1978, relativa a las computadoras, archivos y libertades, usted tiene el derecho de oposición (art.26 de la ley), el acceso (art.34 a 38 Ley), y correcta (artículo 36 de la ley) los datos que le conciernen. Por lo tanto, usted puede pedir que se corrija, complementado, clarificado, actualizado o suprimido información sobre usted que son inexactos, incompletos, engañosos, obsoletos o cuya recogida o de conservación o uso está prohibido.
La información personal sobre los visitantes de nuestro sitio, incluyendo su identidad, son confidenciales.
El jefe del sitio en el honor se compromete a respetar la confidencialidad de los requisitos legales aplicables en Francia y no de revelar dicha información a terceros.


Todo el contenido en este sitio: Copyright © 2024 Elsevier, sus licenciantes y colaboradores. Se reservan todos los derechos, incluidos los de minería de texto y datos, entrenamiento de IA y tecnologías similares. Para todo el contenido de acceso abierto, se aplican los términos de licencia de Creative Commons.