The performance, in thiophene HDS, of a CoMo/Al₂O₃ catalyst was successfully improved through chemical modification of its oxidic precursor by impregnation with 1,5-pentanediol solution. The gas phase activation with a H₂/H₂S mixture was followed by thermogravimetric analysis coupled with a rapid chromatograph; the catalysts were characterized at different steps of the activation using X-ray photoelectron spectroscopy (XPS). It appeared that the addition of the organic agent retards the sulfidation of the supported metals, leading to a simultaneous sulfidation of Co and Mo atoms. This induces the formation of smaller MoS₂ slabs and thus an increase in the number of active CoMoS sites, directly correlated with the better HDS performance of the modified solid. The role of 1,5-pentanediol is likely to inhibit, at low temperature, the adsorption of H₂S on the solid and thus the sulfidation of the supported metals.

La performance d'un catalyseur CoMo/Al₂O₃ en HDS du thiophène a été améliorée grâce à une modification chimique du précurseur oxyde par imprégnation avec une solution de 1,5-pentanediol. L'activation en phase gazeuse avec un mélange H₂/H₂S a été suivie par analyse thermogravimétrique couplée à un chromatographe rapide en phase gaz et les solides ont été caractérisés à différentes étapes de l'activation par spectroscopie de photoélectrons induits par rayons X (XPS). L'addition de cet agent organique induit un retard de la sulfuration des métaux supportés. Ceci se traduit par une sulfuration simultanée des atomes Co et Mo, conduisant à une taille inférieure des feuillets de MoS₂ et donc à une augmentation du nombre de sites actifs CoMoS. Cette augmentation est directement corrélée aux meilleures performances en HDS du solide modifié. Le rôle du 1,5-pentanediol semble donc être d'inhiber l'adsorption d’H₂S sur le solide à basse température, et en conséquence la sulfuration des métaux.