That contribution to transformation plasticity of steels arising from the so-called Greenwood-Johnson mechanism is often described using the model developed by Leblond and coworkers. This model made the assumption of purely plastic behaviour. It is extended here to incorporate viscous effects, which are present during some transformations, especially at high temperatures. The predictions of the original and extended models are compared to experimental results for a material for which the second contribution to transformation plasticity, due to the so-called Magee mechanism, is known to be negligible, and it is shown that the incorporation of viscous effects into the model significantly improves its predictions. To cite this article: Y. Vincent et al., C. R. Mecanique 331 (2003).

La contribution à la plasticité de transformation des aciers due au mécanisme dit de Greenwood-Johnson est souvent décrite à l'aide du modèle de Leblond et coll. Ce modèle faisait l'hypothèse d'un comportement purement plastique. On l'étend ici en incorporant les effets visqueux, présents lors de certaines transformations, particulièrement à haute température. Les prédictions des modèles original et étendu sont comparées à des résultats expérimentaux pour un matériau pour lequel la seconde contribution à la plasticité de transformation, due au mécanisme dit de Magee, est connue pour être négligeable, et l'on montre que l'incorporation des effets visqueux dans le modèle en améliore significativement les prédictions. Pour citer cet article : Y. Vincent et al., C. R. Mecanique 331 (2003).