The dissolution of aluminium in cryolitic melts is the major cause of the loss in current efficiency during the industrial process of aluminium electrolysis. These melts are corrosive and not easy to handle experimentally. Using the laser-heated device, associated with a tightly closed crucible, we have studied different compositions of the NaF-AlF₃-Al system by ²⁷Al, ²³Na and ¹⁹F in situ NMR at 1030 °C. The samples were also characterized after rapid cooling at room temperature by MAS NMR, X-rays diffraction and microscopy in order to describe the structure of the solidified phases. To cite this article: I. Nuta et al., C. R. Chimie 7 (2004).

La dissolution de l'aluminium dans les bains cryolitiques est une des causes principales de faible rendement électrique dans le procédé d'électrolyse de l'aluminium. Ces liquides sont corrosifs et difficiles à manipuler. Avec un système de chauffage par laser associé à un creuset étanche, nous avons étudié différentes compositions du système NaF-AlF₃-Al par RMN de ²⁷Al, ²³Na et ¹⁹F in situ, à 1030°C. Les échantillons ont ensuite été caractérisés, après refroidissement à température ambiante, par RMN MAS, diffraction des rayons X et microscopie, afin de décrire la structure des phases solidifiées. Pour citer cet article : I. Nuta et al., C. R. Chimie 7 (2004).