A systematic investigation on glass formation in the ternary system InF₃-BaF₂- Sc(PO₃)_{3 n} has been carried out. Scandium polyphosphate Sc(PO₃)_{3 n} has been used as a third component in order to investigate the possibilities of obtaining new stable glasses. The above long-chain polyphosphate has been prepared using a specially elaborated cryo-technique, which allowed the preparation of high-purity product. Stable ternary compositions have been obtained within the compositions range (in mol%): 5-75 InF₃, 0-80% BaF₂, 0-50% Sc(PO₃)_{3 n}. Glasses were characterized by Differential Scanning Calorimetry, vibrational spectroscopy (Raman) and ³¹P NMR. Structural features for the glass were put forward. Isolated P(O,F)4 groups or fluoroindated metaphosphate units could be identified depending on glass compositions.

Une étude systématique de la formation vitreuse a été menée dans le système ternaire InF₃-BaF₂- Sc(PO₃)_{3 n}. Le polyphosphate de scandium a été utilisé pour renforcer la stabilité vis-à-vis de la dévitrification. Il est synthétisé par un procédé cryotechnique. Des verres stables ont été obtenus dans les fourchettes de composition suivantes, exprimées en pourcentage molaire : 5-75 InF₃, 0-80 BaF₂, 0-50 Sc(PO₃)_{3 n}. Les verres ont été caractérisés par analyse calorimétrique différentielle, spectroscopie vibrationnelle et résonance magnétique nucléaire du ³¹P. Cette étude met en évidence, selon le domaine de composition, des unités structurales isolées P(O,F)₄ ainsi que des motifs de metaphosphate fluoré.