A comprehensive investigation of aqueous microemulsion polymerization of butyl acrylate at high surfactant concentrations by means of reaction calorimetry and dynamic light scattering revealed unexpected results with regard to polymerization kinetics and colloidal properties of the final latexes. Particularly, with increasing surfactant concentrations, a decrease in the overall rate of polymerization accompanied by an increasing incubation time of the polymerization and increasing average particle sizes in the final latexes has been observed. Based on reviewing former results on microemulsions and microemulsion polymerizations published in the open literature and the presentation of new experimental results an attempt is made to explain the experimental results consistently with a particle nucleation mechanism based on the classical nucleation theory. To cite this article: K. Tauer et al., C. R. Chimie 6 (2003).

L'étude approfondie de la polymérisation radicalaire de l'acrylate de butyle en microémulsion par calorimétrie et diffusion quasi-élastique de la lumière a conduit à des résultats inattendus aussi bien du point de vue de la cinétique de polymérisation que de celui des propriétés colloïdales du latex synthétisé. En particulier, l'augmentation de la concentration en tensioactif s'accompagne d'une diminution de la vitesse globale de polymérisation, de l'augmentation du temps d'incubation de la polymérisation et d'une augmentation de la taille des particules. Au regard de ces résultats et de ceux publiés dans la littérature sur les microémulsions et les polymérisations en microémulsion, une tentative d'explication en accord avec la théorie classique de la nucléation a été élaborée. Pour citer cet article : K. Tauer et al., C. R. Chimie 6 (2003).