This paper focuses on the intergranular and intragranular cobalt repartitions in alumina supported cobalt Fischer–Tropsch catalysts promoted with platinum (0.05–0.1wt.%) with a wide range of cobalt contents (10–25wt.%). The catalysts were characterized at both nano- and micron-scale levels using several characterization techniques. In the calcined catalysts, Co₃O₄ crystalline phase was the major cobalt phase, no hardly reduced cobalt aluminates were detected. The size of the Co₃O₄ crystallites varied from 8 to 12nm.

At the micron-scale range, the catalysts were constituted of grains of 90μm diameter. Scanning electron microscopy (SEM) in combination with energy-dispersive X-ray spectroscopy (EDX) showed the uniform intergranular and intragranular cobalt repartitions in the catalysts. Increase in cobalt content up from 10 to 25wt.% did not alter the cobalt repartition.

Cet article porte sur les répartitions intergranulaire et intragranulaire du cobalt dans les catalyseurs Fischer–Tropsch supportés par l’alumine et promus par du platine (10–25% poids Co et 0.05–0.1% poids Pt). Les catalyseurs ont été caractérisés à l’échelle nano- et micrométrique par une combinaison de techniques physico-chimiques. Dans les catalyseurs calcinés, le Co₃O₄ est la phase principale du cobalt, la taille des cristallites Co₃O₄ variant entre 8 et 12nm. La présence d’aluminate de cobalt n’a pas été détectée. Une étude par microscopie MEB–EDX a montré qu’à l’échelle micrométrique la répartition du cobalt entre les différents grains et à l’intérieur d’un grain des catalyseurs reste homogène même à haute teneur en cobalt.