New polymeric precursors suitable to form boron containing silicon oxycarbide glass were synthesized by the hydroboration reaction of 1,3,5,7-tetramethyl-1,3,5,7-tetravinylcyclotetrasiloxane with borane dimethylsulphide. The obtained polymers denoted as poly(organoborosiloxanes) were characterized by elemental analysis, thermal gravimetric analysis in combination with in situ mass spectrometry (TG/MS), FT-IR and Raman spectroscopy. The polymer-to-ceramic transformation was achieved at 1100 °C in inert argon atmosphere yielding black and X-ray amorphous SiBCO ceramics thermally stable up to 1200 °C. At temperatures exceeding 1300 °C crystallization forming β-SiC was found along with decomposition of the SiBCO matrix. Crystalline silica phases were not formed during annealing of SiBCO up to 1500 °C. To cite this article: V. Liebau et al., C. R. Chimie 7 (2004).

De nouveaux précurseurs du bore contenant du verre d'oxycarbure de silicium ont été synthétisés par la réaction d'hydroboration du 1,3,5,7-tétraméthyl-1,3,5,7-tétravinylcyclotétrasiloxane avec du diméthylsulfure de borane. Les polymères obtenus ont été caractérisés par analyses élémentaires, analyse thermique gravimétrique ainsi que par spectrométrie de masse in situ (ATG/MS), FT-IR et spectroscopie Raman. La transformation du polymère en céramique est réalisée à 1100 °C en atmosphère inerte d'argon et donne des céramiques de SiBCO noires et amorphes sous rayons X et thermiquement stables jusqu'à 1200 °C. Pour des températures supérieures à 1300 °C, la cristallisation aboutissant à β-SiC se produit simultanément à la décomposition de la matrice SiBCO. Jusqu'à 1500 °C, les phases de silice cristallines ne se forment pas pendant le recuit de SiBCO. Pour citer cet article: V. Liebau et al., C. R. Chimie 7 (2004).