We have used 2D hexagonal SBA-15 silicas as templates for the nanofabrication of Mn oxide particles. Despite challenging aspects (several oxidation states of manganese, several polymorphs for each oxidation state), manganese oxides were chosen because of the high economical and environmental significance associated with their ion-exchange, molecular adsorption, electrochemical, magnetic and catalytic properties. We show that single phase MnO_x nanoparticles can be prepared within SBA-15 mesopores. The interest of diffraction and absorption measurements recorded in situ upon calcination to follow the crystallization of these particles at increasing length scales is illustrated. To cite this article: V. Escax et al., C. R. Chimie 8 (2005).

Des nanofils d'oxyde de manganèse ont été obtenus par moulage dans la porosité de silices ordonnées de type SBA-15. La caractérisation de ces oxydes est complexe, car le manganèse peut être présent à différents degrés d'oxydation et différents polymorphes existent pour un même degré d'oxydation. Nous les avons toutefois choisis du fait de leur importance économique et de leurs domaines d'applications variés (adsorption, échange ionique, électrochimie, magnétisme et catalyse hétérogène). Nous avons observé que le dépôt d'un sel précurseur (nitrate de manganèse) par une technique « deux solvants » suivie d'une calcination sous air permet d'obtenir des nanofils polycristallins d'un seul oxyde (MnO₂) moulés dans les pores des silices SBA-15. L'intérêt d'une approche multi-échelles, et donc multi-techniques, couplant des mesures de diffraction et d'absorption pour suivre in situ la cristallisation de ces nanofils est illustré. Pour citer cet article : V. Escax et al., C. R. Chimie 8 (2005).