To improve the hydrogen content of a biomass steam gasification syngas, Water–Gas Shift Fe/CeO₂ catalysts supported on ceramic foams were developed. The impregnation of ceria as washcoat led to an increase in the support surface area (BET) and to the formation of well-dispersed iron particles (XRD and TPR) by iron oxide impregnation. Catalytic tests were performed at atmospheric pressure with minor pressure drops, under a gas mixture similar to that produced at the gasifier outlet. A satisfactory CO conversion and a large increase in H₂ content were reached by adjusting the operating parameters of the WGS and the catalysts’ composition. After-test characterizations indicated in situ catalysts activation with no over-reduction and a positive action of ceria on iron dispersion and sintering prevention.

Des catalyseurs de Water–Gas Shift Fe/CeO₂ supportés sur mousses céramiques ont été développés afin d’améliorer la teneur en hydrogène d’un gaz de synthèse produit par vapogazéification de la biomasse. L’imprégnation d’un washcoat de cérine a conduit à une augmentation de la surface spécifique du support (BET) et à la formation de particules de fer bien dispersées (DRX et TPR) par imprégnation d’oxyde de fer. Des tests catalytiques ont été réalisés à pression atmosphérique avec des pertes de charge minimes sous un mélange gazeux similaire à celui produit dans le gazéifieur. Une bonne conversion du CO et une large augmentation de la teneur en H₂ ont été atteintes en ajustant les paramètres opératoires du WGS et la composition des catalyseurs. Les caractérisations après test ont indiqué une activation in situ du catalyseur sans sur-réduction et une action positive de la cérine sur la dispersion du fer et la prévention du frittage.